Nanoporous characterization of modified humidity-sensitive MgO-Al2O3 ceramics by positron annihilation lifetime spectroscopy method

Abstract

The work was supported by the Ukrainian Ministry of Education and Science. H. Klym thanks Prof. O. Shpotyuk for the fruitful discussion. ; Investigation of nanopores in the humidity-sensitive MgO-Al2O3 ceramics modified at 1100°C for 2 hours was performed using positron annihilation lifetime spectroscopy method. Lifetimes of the third and fourth components of positron annihilation lifetime spectra obtained by four-component fitting procedure were used for calculation of nanopores radii. Transformation in free volumes was studied in ceramics after drying and exposure to water vapor. It is established that the lifetime of the third component decreases and the intensity of this component increases in ceramics exposed to water vapor reflecting ortho-positronium decay in nanopores simultaneously with annihilation in water bubbles. The characteristics of the fourth component (lifetime and intensity) decrease in ceramics exposed to water vapor reflecting ortho-positronium trapping in free-water volume of nanopores. Final drying of the MgO-Al2O3 ceramics results in returning of ortho-positronium lifetimes and intensities to the initial values confirming good desorption of water from nanopores of ceramics. ; Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²