Selective catalytic reduction of nitrogen oxides with ammonia over microporous zeolite catalysts

Abstract

With increasing legislative demands to remove nitrogen oxides (NOx) from automotive diesel exhaust, new catalyst systems are investigated and intensely studied in industry as well in academia. The most prevailing catalytic method of choice is the selective catalytic reduction (SCR) where non-toxic urea is used as a reductant for practical reasons. Usually urea is stored in a separate tank and once injected into the exhaust system it hydrolyses into the more aggressive reductant NH3 and CO2. 4 NH3 + 4 NO + O2 -> 4 N2 + 6 H2O (NH3-SCR reaction) In regions where vanadium is not banned cost effective V2O5/WO3/TiO2 NH3-SCR catalyst systems can be used. Vanadium based are well understood, but they do however not provide stability above ca. 550 °C for longer periods of time. In exhaust treatment systems where the temperature is either high or where high temperature excursions are experienced from e.g. regeneration of particulate filters, zeolite based catalysts are therefore today the most promising candidates as high-temperature stable and non-toxic catalysts for the NH3-SCR reaction. Among the most promising candidates are the Cu- and Fe-based zeolites. Usually Fe based zeolites show good performance in the temperature range 250-500 °C and reasonable stability, whereas Cu-based zeolites show good low-temperature activity in the 180-400 °C range. The presence of copper does however also lead to a lower stability of the catalyst material. Since the low-temperature activity is of paramount importance it is necessary to improve this behavior. Therefore the purpose of this project is to investigate: - The deactivation mechanism of copper based zeolites - The influence of the zeolite framework on stability and activity These investigations should mostly be carried out on model systems such as Cu-ZSM-5 and Cu-IM-5. Recently it was found that zeolite materials with the CHA-type structure show increased hydrothermal stability, most likely originating from the small 8-MR window openings in the structure. Part of the project ...