Experimental and theoretical study of α–Eu2(MoO4)3 under compression

Abstract

The compression process in the α-phase of europium trimolybdate was revised employing several experimental techniques. X-ray diffraction (using synchrotron and laboratory radiation sources), Raman scattering and photoluminescence experiments were performed up to a maximum pressure of 21 GPa. In addition, the crystal structure and Raman mode frequencies have been studied by means of first-principles density functional based methods. Results suggest that the compression process of α-Eu2(MoO4)3 can be described by three stages. Below 8 GPa, the α-phase suffers an isotropic contraction of the crystal structure. Between 8 and 12 GPa, the compound undergoes an anisotropic compression due to distortion and rotation of the MoO4 tetrahedra. At pressures above 12 GPa, the amorphization process starts without any previous occurrence of a crystalline-crystalline phase transition in the whole range of pressure. This behavior clearly differs from the process of compression and amorphization in trimolybdates with β′-phase and tritungstates with α-phase. ; We thank Diamond Light Source for access to beamline I15 (EE1746) that contributed to the results presented here. Part of the diffraction measurements were performed at the 'Servicio Integrado de Difraccion de Rayos X (SIDIX)' of University of La Laguna. This work has been supported by Ministerio de Economia y Competitividad of Spain (MINECO) for the research projects through the National Program of Materials (MAT2010-21270-C04-01/02/03/04, MAT2013-46649-C41/2/3/4-P and MAT2013-43319-P), the Consolider-Ingenio 2010 MALTA (CSD2007-00045), the project of Generalitat Valenciana (GVA-ACOMP/2014/243) and by the European Union FEDER funds. C Guzman-Afonso wishes to thank ACIISI and FSE for a fellowship. J A Sans thanks the FPI and 'Juan de la Cierva' programs for fellowships. ; Guzmán-Afonso, C.; León-Luis, S.; Sans-Tresserras, JÁ.; González -Silgo, C.; Rodríguez-Hernández, P.; Radescu, S.; muñoz, A. (2015). Experimental and theoretical study of α–Eu2(MoO4)3 under compression. ...