"Development of experimental dental prostheses formulations based on methacrylic resins. The effect Study, on the degree of conversion (DC) and volumetric shrinkage (VS), of four crosslinking agents: DEDGMA, TEGDMA, TETRAEGDA and TMPTA and four radiopacifying mineral fillers: ZrO2, TiO2, SrO and BaO2. The experimental resins are compared to commercial products. The (DC) determination of the experimental and commercial resins was carried out by FTIR in ATR mode. The (VS) was determined experimentally by the Archimed's method. Chemical structure and weight content of crosslinking agents affected (DC) and (VS). (DC) and (VS) increased with the crosslinking agent chain length and weight contents. Additionally, whatever filler contents and metal nature, (DC) values remains ≥ 99.5%, in accordance with the standards required for residual monomers level tolerated in dental prostheses (<0.45%). (VS) values varied between 4,8 and 10,8%. For two commercial resins, (DC) values were less than 99% while (VS) was in accordance with the standards (5-6%): 6.2% for Major base and 4.3% for Hiflex H."

"Organosilanes bearing alkoxysilane are widely used in sol-gel process. In this process, the hydrolysis reaction is usually carried out in aqueous or hydroalcoholic solutions and the condensation reaction requires high temperatures. The hydrolysis of the alkoxysilanes in the presence of water is fast and can be considered as complete. The obtained silanols can then condensate into oligomers by a much slower reaction that depends on temperature. Our objective is to devise a simple synthesis way for grafting such coupling agent onto the mineral fillers surface without using solvent and heating. Mineral fillers are used as reinforcement in dental composites based on Bis-GMA/TEGDMA. The way developed in this work involves a photoinitiated sol-gel process. It consists in using a photoacid generator to activate the hydrolysis and condensation reactions under atmospheric humidity. Mineral oxides usually used in dental materials were chosen as inorganic filler: the zirconia (ZrO2) which is a radiopacifiant agent and the alumina (Al2O3) which allows improving the mechanical properties of the composite. A kinetic study of the self-condensation of the 3-MPS used as coupling agent in the presence of Irgacure 250 ® as photoacid generator was carried out and the operating conditions (irradiation intensity and time) of the functionalization reaction were optimized. Grafted fillers were characterized by FTIR spectroscopy and thermogravimetic analysis. FTIR and TGA analyses of the particles after treatment allow confirming the grafting. Compared to the conventional way, the photoinitiated process proves to be faster, easier, less expensive in energy, and much more efficient in terms of 3-MPS grafted quantity. "