Suchergebnisse

In this work, metal-insulator-semiconductor structures were fabricated in order to study different types of insulators, namely, aluminum oxide (Al2O3), silicon nitride, and silicon oxide (SiOx) to be used as passivation layers in Cu(In,Ga)Se-2 (CIGS) thin-film solar cells. The investigated stacks consisted of SLG/Mo/CIGS/insulator/Al. Raman scattering and photoluminescence measurements were done to verify the insulator deposition influence on the CIGS surface. In order to study the electrical properties of the CIGS-insulator interface, capacitance versus conductance and voltage (C-G-V) measurements were done to estimate the number and polarity of fixed insulator charges (Q(f)). The density of interface defects (D-it) was estimated from capacitance versus conductance and frequency (C-G-f) measurements. This study evidences that the deposition of the insulators at high temperatures (300 degrees C) and the use of a sputtering technique cause surface modification on the CIGS surface. We found that, by varying the SiOx deposition parameters, it is possible to have opposite charges inside the insulator, which would allow its use in different device architectures. The material with lower Dit values was Al2O3 when deposited by sputtering. ; This work was supported by European Union's Horizon 2020 research and innovation programme ARCIGS-M project under Grant 720887. The work of J. M. V. Cunha and P. M. P. Salome was supported by the Fundacao para a Ciencia e a Tecnologia (FCT) through the project IF/00133/2015. The work of J. P. Teixeira and J. P. Leitao was supported by the FCT through the project UID/CTM/50025/2013. The work of B. Vermang was supported by the European Research Council under the European Union's Horizon 2020 research and innovation programme under Grant 715027.