Suchergebnisse

T. G. acknowledges the ERDF PostDoc project No. 1.1.1.2/VIAA/1/16/215 (1.1.1.2/16/I/001). K. S. and K. L. acknowledge the Latvian National Research Program IMIS2. The authors from Vinča Institute of Nuclear Sciences acknowledge the financial support of the Ministry of Education, Science and Technological Development of the Republic of Serbia (Project No: 45020 and 172056 ). ; Nanoparticles (5 nm) and nanorods (2 nm × 15 nm and 4 nm × 20 nm) of monoclinic monazite LaPO4:Eu3+ were prepared by reverse micelle and co-precipitation techniques. Effects of the particle size and surface defects on the intensity of luminescence and the emission spectrum shapes were analyzed by high resolution spectroscopy under laser (266 nm) and X-rays excitation. All synthesized LaPO4:Eu3+ samples showed similar spectral features with characteristic Eu3+ ions emission bands: 5D0→7F0 centered at 578.4 nm, magnetic-dipole transition 5D0→7F1 at 588–595 nm, electric-dipole transition 5D0→7F2 at 611.5–620.5 nm, 5D0→7F3 at (648–652 nm) and 5D0→7F4 at (684–702.5 nm), with the most dominant electric-dipole 5D0→7F2 transition. Additionally, the thermally stimulated luminescence was studied for the most dominant peak at 611.5 nm. It was shown that the Eu3+ doping creates traps in all samples. Two prominent and well resolved glow peaks at 58.7 K and 172.3 K were detected for 5 nm nanoparticles, while low-intensity glow-peaks at 212.1 K and 212.2 K were observed in the X-rays irradiated nanorods. Displayed glows could be attributed to free and bound electrons and holes or to the recombination of electrons of ionized oxygen vacancies with photogenerated holes. To obtain information about the processes and specific defect type it is necessary to carry out additional analysis for all synthesized samples. The glow curves were analyzed and trap parameters were estimated and discussed throughout the paper. ; ERDF PostDoc project No. 1.1.1.2/VIAA/1/16/215 (1.1.1.2/16/I/001); IMIS2; Ministry of Education, Science and Technological Development of the Republic of Serbia (Project No: 45020 and 172056 ); Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²

The authors acknowledge the financial support of the Ministry of Education, Science and Technological Development of the Republic of Serbia (Projects nos. 45020 and 172056). T.G acknowledges to the ERDF PostDoc project No. 1.1.1.2/VIAA/1/16/215 (1.1.1.2/16/I/001). ; This paper provides the detailed study of (nano)particle's size effect on structural and luminescent properties of LaPO4:Eu3+ synthesized by four different methods: high temperature solid-state, co-precipitation, reverse micelle and colloidal. These methods delivered monoclinic monazite-phase submicron particles (> 100 nm), 4 × 20 nm nanorods and 5 nm spheres (depending on the annealing temperature), 2 × 15 nm nanorods, and ultra-small spheres (2 nm), respectively. The analysis of emission intensity dependence on Eu3+ concentration showed that quenching concentration increases with a decrease of the particle size. The critical distance for energy transfer between Eu3+ ions is found to be 18.2 Å, and the dipole-dipole interaction is the dominant mechanism responsible for the concentration quenching of emission. With the increase in Eu3+ concentration, the unit-cell parameter slightly increases to accommodate larger Eu3+ ions at sites of smaller La3+ ions. Photoluminescent emission spectra presented four characteristic bands in the red spectral region: at 592 nm (5D0→7F1), at 612 nm (5D0→7F2), at 652 nm (5D0→7F3) and at 684 nm (5D0→7F4), while in small colloidal nanoparticles additional emission bands from host defects appear at shorter wavelengths. Intensities of f-f electronic transitions change with particles size due to small changes in symmetry around europium sites, while emission bandwidths increase with the reduction of particle size due to increased structural disorder. Judd-Ofelt analysis showed that internal quantum yield of Eu3+ emission is strongly influenced by particle's morphology. ; Ministry of Education, Science and Technological Development of the Republic of Serbia (Projects nos. 45020 and 172056); ERDF PostDoc project No. 1.1.1.2/VIAA/1/16/215 (1.1.1.2/16/I/001); Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²

All authors acknowledge to the COST Action CM1403: The European upconversion network - from the design of photon-upconverting nanomaterials to biomedical applications (2014–2018). The authors from the University of Belgrade acknowledge the financial support of the Ministry of Education, Science and Technological Development of the Republic of Serbia (Project Nos. 45020 and 172056 ). K. S. acknowledges the Latvian National Research Program IMIS2 (Grant No. 302/2012 ). T. G. acknowledges the ERDF PostDoc project No. 1.1.1.2/VIAA/1/16/215 ( 1.1.1.2/16/I/001 ). ; In recent years, there exists a tendency in research of up-conversion materials to shift excitation from 980 nm to shorter wavelengths. Here, in order to produce up-conversion luminescence emission of GdVO4-based materials under 808 nm excitation, polycrystalline powders of GdVO4:Er3+/Nd3+ and GdVO4:Ho3+/Nd3+ were successfully prepared by a high-temperature solid-state reaction technique. The prepared powders were highly crystalline with a single-phase zircon-type GdVO4 structure and consisted of micrometer-sized irregular spherical particles (2–6 μm in diameter). In all studied samples, visible up-conversion luminescence was successfully achieved under 808 nm illumination. Near-infrared pumping produced emission bands in the green, yellow-orange and green regions of the visible spectrum. The bands in the green and red regions of GdVO4: Er3+/Nd3+ as well as GdVO4:Ho3+/Nd3+ were, respectively, characteristic of Er3+ and Ho3+ ions. The dominant band originating from the 4G7/2 → 4I11/2 transition in Nd3+ ions was observed around 597 nm in all samples. ; COST Action CM1403 (2014–2018); Ministry of Education, Science and Technological Development of the Republic of Serbia (Project Nos. 45020 and 172056 ); Latvian National Research Program IMIS2 (Grant No. 302/2012 ); ERDF PostDoc project No. 1.1.1.2/VIAA/1/16/215 ( 1.1.1.2/16/I/001 ); Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²