Suchergebnisse

We are grateful to Prof. E. Kotomin for useful discussions. The research leading to these results has received funding from the ERAF (2017) Project, while A. I. Popov thanks IMIS-2 for the funding support. ; In the present work, possibilities of the extraction–pyrolysis method (EPM) to produce FePt nanoparticles with the face-centered tetragonal (fct) phase were studied. A mixture of fine-disperse powder of carbonyl iron and n-trioctylam-monium hexachloroplatinate [(С8Н17)3NH]2PtCl6 solution in toluene, preliminary produced by the solvent extraction method, is used as a precursor. Precursors with a different molar ratio of metals were used. The performed investigations show that as a result of pyrolysis in the air (Tpyr = 600°C, tanneal = 30 min), a FePt alloy with the fct phase is produced. Moreover, such phases as FePt3 and/or Fe3Pt with the cubic structure may be also present in the final products. The phase composition of the produced samples depends on the Fe:Pt molar ratio in the precursor. An increase of the fct phase part with the growth of the iron content from 40 to 60 mol% is observed. Also, with the Fe80%Pt20% molar ratio of the metals in the precursor, only the ordered fct phase along with a small amount of hematite and iron chloride exists in the produced sample. Magnetic measurements confirm the fct-FePt phase formation in all produced samples and evidence that the coercivity exceeds the value (3 kOe) at the 50 mol% Fe concentration in the precursor and significantly decreases with increasing the Fe concentration to 80 mol%. ; ERAF; IMIS-2; Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²

The work has been done in frame of the TransFerr project. It has received funding from the European Union's Horizon 2020 research and innovation program under the Marie Sklodowska-Curie grant agreement No. 778070. This research was also supported by Latvian Research Council project lzp-2018/1-0214. A.I.P. appreciates support from the Estonian Research Council grant (PUT PRG619). ; Interest in magnetic nanoparticles is primarily due to their practical use. In this work, for the production of nanocrystalline powders of pure and gadolinium doped iron oxides, the extraction-pyrolytic method (EPM) was used. As a precursor, either iron-containing extract (iron (III) caproate in caproic acid) or its mixture with gadolinium-containing extract (gadolinium (III) valerate in valeric acid) was used. The mixed precursor contained 0.5 mol %, 2.5 mol %, 12.5 mol %, 50 mol %, and 75 mol % gadolinium in relation to the iron content. The formation of iron oxide phases, depending on the preparation conditions, was investigated. According to the results obtained, it was demonstrated that the presence of more than 2.5 mol % gadolinium additive in the mixed precursor inhibits the magnetite-to-hematite transformation process during thermal treatment. Produced samples were characterized by XRD and SEM methods, and the magnetic properties were studied. ; H2020 Marie Sklodowska-Curie grant agreement No. 778070; Latvian Science Council project lzp-2018/1-0214; Estonian Research Council grant (PUT PRG619); Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²

The present study has been supported by the Latvian National Research Program IMIS2. One of us, IS, was supported by MES RF RFMEFI61615X0064. ; X-ray diffraction, micro-Raman and the Fourier transform infrared spectroscopies as well as magnetometry measurements were performed on nanosized manganese oxides to probe their phase composition and magnetic properties. It was shown that the XRD method is less sensitive to phase composition of manganese oxide samples than spectroscopic methods. While in some samples the XRD method recognised only the manganosite MnO phase, the Raman and FT-IR methods revealed additionally the presence of the hausmannite Mn3O4 phase. ; Ministry of Education and Science RF RFMEFI61615X0064; Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²