The aim of the work was to check how the introduction of alkali and cobalt ions into a manganese structure can affect the structural disorder and, in consequence, lead to the changes (improvements) of magnetic properties. The high-pressure sintering technique was applied to check if the external factor can modify the magnetization of manganites. Nanocrystalline La0.9A0.1Mn0.9Co0.1O3 (where A is Li, K, Na) powders were synthesized by the combustion technique. The respective powders were used for nanoceramics preparation by the high-pressure sintering technique. The structure and morphology of the compounds were studied by X-ray powder diffraction, scanning electron microscopy and energy-dispersive X-ray spectroscopy. Magnetization studies for all compounds were performed in order to check the changes induced by either codoping or the sintering pressure. It was found that the type of the dopant ion and sintering pressure produced significant changes to the magnetic properties of the studied compounds. Alkali ions lead to the stabilization of Co ions in the +2 oxidation state and the formation of positive exchange interactions Mn3+–Mn4+ and Co2+–Mn4+ and the subsequent increase in remanent magnetization. High sintering pressure leads to a decrease in grain size and reduction of long-range ferromagnetic order and lower magnetization. © 2020 by the authors. Licensee MDPI, Basel, Switzerland. ; This project has received funding from the European Union's Horizon 2020 research and innovation programme under the Marie Skłodowska‐Curie grant agreement No 778070–TransFerr–H2020‐MSCA‐RISE‐ 2017. Part of this work was developed within the scope of the project CICECO‐Aveiro Institute of Materials, UIDB/50011/2020 and UIDP/50011/2020, financed by national funds through the Portuguese Foundation for Science and Technology/MCTES. The equipment of the Ural Center for Shared Use "Modern nanotechnology" UrFU was used. The work has been supported in part by the Ministry of Science and Higher Education of the Russian Federation under Project № FEUZ‐2020‐0054.

Samarium substituted bismuth ferrite (BiFeO3) ceramics prepared by sol-gel synthesis method were studied using both local scale and microscopic measurement techniques in order to clarify an evolution of the crystal structure of the compounds across the morphotropic phase boundary region. X-ray diffraction analysis, transmission and scanning electron microscopies, XPS, EDS/EDX experiments and piezoresponse force microscopy were used to study the structural transitions from the polar active rhombohedral phase to the anti-polar orthorhombic phase and then to the non-polar orthorhombic phase, observed in the Bi1−xSmxFeO3 compounds within the concentration range of 0.08 ≤ x ≤ 0.2. The results obtained by microscopic techniques testify that the compounds in the range of 0.12 ≤ x ≤ 0.15 are characterized by two phase structural state formed by a coexistence of the rhombohedral and the anti-polar orthorhombic phases; two phase structural state observed in the compounds with 0.15