Suchergebnisse

The work was supported by the ERDF funding in Estonia granted to the Center of Excellence TK141 "Advanced materials and high-technology devices for sustainable energetics, sensorics and nanoelec-tronics" (project No. 2014-2020.4.01.15-0011). Partial support of the projects from the Ministry of Education, Youth and Sports of the Czech Republic no. LO1409, LM2015088 and CZ.02.1.01/0.0/0.0/16 013/ 0001406 is also gratefully acknowledged. ; Temperature dependences of the photoluminescence and X-ray excited luminescence intensity and thermally stimulated luminescence glow curves are measured in the 4.2–300 K temperature range for the undoped and Ce3+ - doped Gd3(Ga,Al)5O12 crystals. The conclusion is made that no low-temperature quenching of the Ce3+ - related photoluminescence takes place. In both the undoped and the Ce3+ - doped crystals, temperature dependences of the X-ray excited recombination luminescence intensity correlate with the position and shape of thermally stimulated luminescence glow curve peaks of the hole origin. Low-temperature quenching of the X-ray excited luminescence in these crystals is explained by the fact that at low temperatures, free holes are trapped at oxygen ions while electrons are trapped at various intrinsic defects. In Ce3+ - doped Gd3(Ga,Al)5O12 crystals, thermally stimulated release of the trapped holes and electrons and their subsequent recombination at Ce3+ ions result in the enhancement of the Ce3+ - related electron recombination luminescence with the increasing temperature in the 10–180 K range. ; ERDF TK141 No. 2014-2020.4.01.15-0011; Ministry of Education, Youth and Sports of the Czech Republic no. LO1409, LM2015088 and CZ.02.1.01/0.0/0.0/16 013/ 0001406; Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²

The work was supported by the Institutional Research Funding IUT02-26 of the Estonian Ministry of Education and Research and the project 16-15569S of the Czech Science Foundation. ; Luminescence characteristics of Ce3+ - doped Gd3GaxAl5-xO12 single crystals with different Ga contents (x = 1, 2, 3, 4, 5) are studied in the 9–500 K temperature range. The spectra of the afterglow, photoluminescence, radioluminescence, and thermally stimulated luminescence (TSL) of each crystal coincide. The increase of the Ga content results in the high-energy shift of the spectra while the radioluminescence intensity at 9 K remains practically constant up to x = 4. No Ce3+ emission is observed in case of x = 5. The total TSL intensity drastically increases, reaches the maximum value around x = 2–3, and then decreases due to the thermal quenching of the Ce3+ emission. The TSL glow curve maxima are gradually shifting to lower temperatures, and the dependence of the maxima positions and the corresponding trap depths on the Ga content is close to linear. However, the activation energy of the TSL peaks creation under irradiation of the crystals in the 4f – 5d1 absorption band of Ce3+ decreases drastically with the increasing Ga content (especially in the range of x = 1–2), and this dependence is found to be strongly nonlinear. Possible reasons of the nonlinearity are discussed. ; Estonian Ministry of Education and Research IUT02-26; Czech Science Foundation 16-15569S; Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union's Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²