Suchergebnisse

Niobium doped dititanium trioxide (Ti2O3:Nb) films were deposited on glass substrates, through grid-assisted magnetron sputtering. The Ti2O3:Nb films were characterized by X-ray diffraction (XRD), electrical conductivity and optical properties. Film deposition was carried out in two different substrate bias modes: DC and unipolar pulsed. Results show that the negative-pulsed mode improves conductivity and crystallinity. The XRD results show peaks corresponding crystallographic planes of Ti2O3. No niobium oxide NbxOy peaks were observed, which indicates that niobium oxide if formed, is amorphous, and/or substituted Nb atoms remain in a solid solution within the Ti2O3 structure. It was observed that "as-deposited" Ti2O3:Nb films (without post annealing) are transparent and electrical conductive, with transmittance that reaches 60% in the visible light wavelength despite the considerable thickness of the film and a miminum resistivity of 2x10-2 Ω.cm which indicates that there is potential for application as Transparent Conductive Oxide (TCO). ; This study was supported by the Government of the State of Santa Catarina through the FUMDES and FAPESC ...

The fabrication of highly transparent piezoelectric transducers is of increasing interest in the scientific and technological community. In this work, polymer based piezoelectric transducers were fabricated by the direct deposition of each layer forming the transducer on the desired substrate, avoiding the use of coupling layers. Transparent conductive oxide (TCO) electrodes were deposited by magnetron sputtering and piezoelectric films based on the copolymer poly(vinylidene fluoride-co-trifluoroethylene) (P(VDF-TrFE)) were deposited by spin-coating. All layers were processed and characterized to obtain a highly transparent piezoelectric P(VDF-TrFE) transducer with a strong adhesion between layers and preserving the piezoelectric response of the copolymer film. Indium tin oxide (ITO), gallium-doped zinc oxide (GZO) and aluminium-doped zinc oxide (AZO) were evaluated, and the best performance was obtained with AZO. The optimized transducer features an optical transmittance higher than 75% in the visible spectral range and a piezoelectric coefficient vertical bar d(33)vertical bar of 34 pC.N-1. ; The authors thank the FCT-Fundacao para a Ciencia e Tecnologia-for financial support under framework of the Strategic Funding UID/FIS/04650/2013, project PTDC/EEI-SII/5582/2014 and project UID/EEA/04436/2013 by FEDER funds through the COMPETE 2020-Programa Operacional Competitividade e Internacionalizacao (POCI) with the reference project POCI-01-0145-FEDER-006941. Funds provided by FCT in the framework of EuroNanoMed 2016 call, Project LungChek ENMed/0049/2016 are also gratefully acknowledged. VFC also thanks the FCT for the grant SFRH/BPD/98109/2013. Finally, the authors acknowledge funding by the Spanish Ministry of Economy and Competitiveness (MINECO) through the project MAT2016-76039-C4-3-R (AEI/FEDER, UE) and from the Basque Government Industry Department under the ELKARTEK and HAZITEK programs. ...

ZnO doped with Cu thin films were deposited on indium tin oxide coated glass substrates by electrodeposition using an electrolyte consisting of Cu and Zn perchlorates dissolved in dimethylsulfoxide. The Cu/Zn ratio measured in the thin films is about twice the Cu/Zn ratio present in the starting electrolyte. Irrespective of the Cu content, all the ZnO:Cu films exhibit a hexagonal wurtzite structure typical of ZnO with a preferential orientation along (002) direction. The p-type behaviour of ZnO:Cu films is inferred from the change in the sign of the photocurrent observed for Cu concentrations greater than 2%. Furthermore, a p-n homojunction with a rectifying factor 22 were prepared by electrodepositing of ZnO/ZnO:Cu layers. ; This work was supported by the Spanish Government through MCINN grant ...

Applications of coloured thin films can be found on the production of high-quality consumer products, such as eyeglass frames, wristwatch casings and wristbands. These components should possess scratch and corrosion resistant surfaces through the desired lifetime. Recently, metal oxynitrides, MeNxOy (Me = early transition metal) were proposed for decorative applications. In these materials, variations on the amount of oxygen allow the film properties to be tailored, originating a wide range of colours. Additionally, these materials should also fulfil the wear and corrosion requirements above referred. In the present work the corrosion behaviour of single layered zirconium oxynitride, ZrNxOy films, immersed in artificial sweat solutions, is described. Films were produced by rf reactive magnetron sputtering at a constant substrate temperature of 300 ºC, from a pure Zr target. The main processing variable was the flow rate of reactive. The corrosion resistance was evaluated by potentiodynamic polarisation tests and Electrochemical Impedance Spectroscopy (EIS) at different immersion times, at room temperature. The corrosion resistance of the films is strongly affected by the O/N ratio. A slight tendency to improving the corrosion resistance of the films was found with the increasing in the atomic fraction of oxygen. Nevertheless, pitting was found in all samples. However, the amount of pits seems to be strongly dependent not only on the composition of the film, but also on the processing-induced defects distribution. ; European Union, FCT- Portugal and European community ...