Suchergebnisse

The correlation between the synthesis modes, chemical composition, crystal structure, surface microstructure, and also the mechanical properties of thin nanostructured Ni – Fe films has been studied. Thin Ni–Fe films on the Si with Au sublayer were obtained using electrolyte deposition with different current modes: direct current and three pulsed modes with pulse duration of 1 s, 10–3 and 10–5 s. It is shown that a decrease in the pulse duration to 10–5 s leads to an increase in the film elastic modulus and the hardness due to the small grain size and a large number of grain boundaries with increased resistance to plastic deformation. The effect of heat treatment at 100, 200, 300, and 400 °C on the surface microstructure and micromechanical properties of the films was investigated. An increase in grain size from 6 to 200 nm was found after heat treatment at 400 °C which, in combination with interfusion processes of the half-layer material, led to a significant decrease in hardness and elastic modulus. Ni–Fe films with improved mechanical properties can be used as coatings for microelectronic body for their electromagnetic protection.

Inorganic-based nanoelements such as nanoparticles (nanodots), nanopillars and nanowires, which have at least one dimension of 100 nm or less, have been extensively developed for biomedical applications. Furthermore, their properties can be varied by controlling such parameters as element shape, size, surface functionalization, and mutual interactions. In this study, Ni-alumina nanocomposite material was synthesized by the dc-Ni electrodeposition into a porous anodic alumina template (PAAT). The structural, morphological, and corrosion properties were studied using x-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), and electrochemical techniques (linear sweep voltammetry). Template technology was used to obtain Ni nanopillars (NiNPs) in the PAAT nanocomposite. Low corrosion current densities (order of 0.5 μA/cm2) were indicators of this nanocomposite adequate corrosion resistance in artificial physiological solution (0.9% NaCl). A porous anodic alumina template is barely exposed to corrosion and performs protective functions in the composite. The results may be useful for the development of new nanocomposite materials technologies for a variety of biomedical applications including catalysis and nanoelectrodes for sensing and fuel cells. They are also applicable for various therapeutic purposes including targeting, diagnosis, magnetic hyperthermia, and drug delivery. Therefore, it is an ambitious task to research the corrosion resistance of these magnetic nanostructures in simulated body fluid. © 2020 by the authors. Licensee MDPI, Basel, Switzerland. ; Government Council on Grants, Russian Federation ; Belarusian Republican Foundation for Fundamental Research, BRFFR: Ф18Д-007 ; 20163522 ; Funding: The work was performed with support of State Scientific and Technical Program "Nanotech" (ГБЦ No 20163522), Belarusian Republican Foundation for Fundamental Research (Grant No. Ф18Д-007), Act 211 of Government of Russian Federation (contract No. 02.A03.21.0011). Additionally, the work was partially supported by the Grant of World Federation of Scientists (Geneva, Switzerland).

The densely packed arrays of Ni nanowires of 70 nm diameter and 6-12 μm length were obtained via electrodeposition into porous alumina membranes (PAAMs) of 55-75 μm thickness. The morphology, microstructure and magnetic properties between the room and liquid-helium temperature of Ni nanowires in PAAMs have been investigated using scanning electron microscopy, X-ray diffraction and vibrating sample magnetometry. The crystal structure of the Ni nanowires is fcc with (220) preferred orientation. The magnetic characteristics of the Ni nanowires in PAAMs were compared with the same characteristics of bulk Ni and with other researchers' data. The effect of the porous alumina membrane and the Ni nanowires synthesis conditions on the magnetic characteristics of Ni nanowire arrays has been studied. The coercivity reached more than 750 kOe and the squareness ratio up to 0.65 under the proposed optimal synthesis conditions for Ni nanowires. Magnetic parameters of the densely packed arrays of Ni nanowires allow using them in magnetic recording media, hard disk drives, storage systems and sensors. In addition, such structures are of considerable interest for basic research on nanomagnetism which is significantly different from the magnetic properties of bulk and thin films materials. © The Royal Society of Chemistry. ; The work was performed with support of State Scientic and Technical Program "Nanotech" (task GBx no 20163522 and no. 2.34), Branch Scientic and Technical Program "Nanotechnology and Nanomaterials" (task no. 1), Act 211 of Government of Russian Federation (contract No. 02.A03.21.0011). Dmitry Lyakhov and Dominik Michels are partially supported by KAUST (baseline funding).

The paper considers the problem of the impact of low-frequency electromagnetic fields (EMF) generated by electric vehicles (EV) and household appliances on humans in modern society. The data on the effect of EMF on human health and regulatory documents establishing requirements for electromagnetic safety are presented. The method of electromagnetic shielding and materials for the implementation of this method are considered as a promising method for solving the problem. The levels of electromagnetic radiation from a number of EV and household electrical appliances have been experimentally measured. The efficiency of electromagnetic shielding of materials based on single-layer coatings of Ni80Fe20 alloys, multilayer film structures Ni80Fe20/Cu and amorphous metal alloys AMAG172 has been estimated using a computational method. It is shown that electromagnetic screens based on these materials significantly reduce the levels of exposure to EMF of EV and household electrical appliances on humans, which allows us to approach the hygienic standards recommended by doctors and meet the requirements of regulatory documents on remote control.

The effect of microstructure on the efficiency of shielding or shunting of the magnetic flux by permalloy shields was investigated in the present work. For this purpose, the FeNi shielding coatings with different grain structures were obtained using stationary and pulsed electrodeposi-tion. The coatings' composition, crystal structure, surface microstructure, magnetic domain struc-ture, and shielding efficiency were studied. It has been shown that coatings with 0.2–0.6 µm grains have a disordered domain structure. Consequently, a higher value of the shielding efficiency was achieved, but the working range was too limited. The reason for this is probably the hindered movement of the domain boundaries. Samples with nanosized grains have an ordered two-domain magnetic structure with a permissible partial transition to a superparamagnetic state in regions with a grain size of less than 100 nm. The ordered magnetic structure, the small size of the domain, and the coexistence of ferromagnetic and superparamagnetic regions, although they reduce the maxi-mum value of the shielding efficiency, significantly expand the working range in the nanostruc-tured permalloy shielding coatings. As a result, a dependence between the grain and domain structure and the efficiency of magnetostatic shielding was found. © 2021 by the authors. Licensee MDPI, Basel, Switzerland. ; This research was funded by the European Union?s Horizon 2020 research and innovation programme under the Marie Sklodowska-Curie grant number 861145. And The APC was funded by the European Union?s Horizon 2020 research and innovation programme under the Marie Sklodowska-Curie grant agreement no. 861145.

Bi nanocrystalline films were formed from perchlorate electrolyte (PE) on Cu substrate via electrochemical deposition with different duration and current densities. The microstructural, morphological properties, and elemental composition were studied using scanning electron microscopy (SEM), atomic force microscopy (AFM), and energy-dispersive X-ray microanalysis (EDX). The optimal range of current densities for Bi electrodeposition in PE using polarization measurements was demonstrated. For the first time, it was shown and explained why, with a deposition duration of 1 s, co-deposition of Pb and Bi occurs. The correlation between synthesis conditions and chemical composition and microstructure for Bi films was discussed. The analysis of the microstructure evolution revealed the changing mechanism of the films' growth from pillar-like (for Pb-rich phase) to layered granular form (for Bi) with deposition duration rising. This abnormal behavior is explained by the appearance of a strong Bi growth texture and coalescence effects. The investigations of porosity showed that Bi films have a closely-packed microstructure. The main stages and the growth mechanism of Bi films in the galvanostatic regime in PE with a deposition duration of 1–30 s are proposed. © 2020 by the authors. Licensee MDPI, Basel, Switzerland. ; Government Council on Grants, Russian Federation ; 2.34 ; Funding: The work was performed with support of State Scientific and Technical Program "Nanotech" (task No. 2.34), Branch Scientific and Technical Program "Nanotechnology and Nanomaterials" (task No. 1), Act 211 of Government of Russian Federation (contract No. 02.A03.21.0011). Additionally, the work was partially supported by the Grant of World Federation of Scientists (Geneva, Switzerland).

Herein, we investigated the correlation between the chemical composition, microstructure, and microwave properties of composites based on lightly Tb/Tm-doped Sr-hexaferrites (SrTb0.01Tm0.01Fe11.98O19) and spinel ferrites (AFe2O4, A = Co, Ni, Zn, Cu, or Mn), which were fabricated by a one-pot citrate sol-gel method. Powder XRD patterns of products confirmed the presence of pure hexaferrite and spinel phases. Microstructural analysis was performed based on SEM images. The average grain size for each phase in the prepared composites was calculated. Comprehensive investigations of dielectric properties (real (ε′) and imaginary parts (ε′′) of permittivity, dielectric loss tangent (tan(δ)), and AC conductivity) were performed in the 1-3 × 106Hz frequency range at 20-120 °C. Frequency dependency of microwave properties were investigated using the coaxial method in frequency range of 2-18 GHz. The non-linear behavior of the main microwave properties with a change in composition may be due to the influence of the soft magnetic phase. It was found that Mn- and Ni-spinel ferrites achieved the strongest electromagnetic absorption. This may be due to differences in the structures of the electron shell and the radii of the A-site ions in the spinel phase. It was discovered that the ionic polarization transformed into the dipole polarization. © The Royal Society of Chemistry 2020. ; 2020-164-IRMC ; 2018-IRMC-S-2 ; Ministry of Science and Higher Education of the Russian Federation ; The authors highly acknowledged the nancial supports provided by the Institute for Research and Medical Consultations (Project application No. 2018-IRMC-S-2) and by the Deanship for Scientic Research (Project application No. 2020-164-IRMC) of Imam Abdulrahman Bin Faisal University (Saudi Arabia). M. S. acknowledges the Ministry of Science and Higher Education of the Russian Federation State assignment 2020– 2022 No. FSMR-2020-0018 (Proposal mnemonic code 0719-2020-0018). The work was partially supported by Act 211 Government of the Russian Federation, contract No. 02.A03.21.0011.

Nanostructured NiFe film was obtained on silicon with a thin gold sublayer via pulsed electrodeposition and annealed at a temperature from 100 to 400◦C in order to study the effect of heat treatment on the surface microstructure and mechanical properties. High-resolution atomic force microscopy made it possible to trace stepwise evolving microstructure under the influence of heat treatment. It was found that NiFe film grains undergo coalescence twice—at ~100 and ~300°C—in the process of a gradual increase in grain size. The mechanical properties of the Au/NiFe nanostructured system have been investigated by nanoindentation at two various indentation depths, 10 and 50 nm. The results showed the opposite effect of heat treatment on the mechanical properties in the near-surface layer and in the material volume. Surface homogenization in combination with oxidation activation leads to abnormal strengthening and hardening-up of the near-surface layer. At the same time, a nonlinear decrease in hardness and Young's modulus with increasing temperature of heat treatment characterizes the internal volume of nanostructured NiFe. An explanation of this phenomenon was found in the complex effect of changing the ratio of grain volume/grain boundaries and increasing the concentration of thermally activated diffuse gold atoms from the sublayer to the NiFe film. © 2020 by the authors. Licensee MDPI, Basel, Switzerland. ; Funding: The work was supported by Act 211 Government of the Russian Federation, contract № 02.A03.21.0011.